Round Wires are brought to hardness and thickness values ​​by rolling and annealing processes, washing and annealing processes are applied.

Round Wires, produced in desired diameters from 0.20 mm to 20 mm, can be produced wrapped on coils or reels weighing up to 3,000 kg.

  • Electrical and Thermal Conductivity
  • Corrosion and Wear Resistance
  • Resistance
  • Cold Forming and Machinability
  • Soldering, Welding and Coating Compliance

Alloys We Produce

Germany
DIN
Europa
EN Sembol
International Standard
Organisation ISO Symbol
USA
UNS
Japan
JIS
France
NS
United Kingdom
BS
CuZn15 CuZn15 CuZn15 C23000 C 2300 CuZn15 CZ102
CuZn20 CuZn20 CuZn20 C24000 C 2400 CuZn20 CZ103
CuZn30 CuZn30 CuZn30 C26000 C 2600 CuZn30 CZ106
CuZn33 CuZn33 CuZn35 C26800 C 2680 CuZn33 CZ107
CuZn37 CuZn37 CuZn37 C27400 C 2720 CuZn37 CZ108
CuNi12Zn24 CuNi12Zn24 CuNi12Zn24 C75700 C 7521 CuNi12Zn24 NS104
Alloy Alloy No. Cu (%) Zn (%) Al (%) Fe (%) Ni (%) Pb (%) Sn (%) Mn (%) Density
(Kg/dm³)
CuZn15 CW502L min.
max.
84,0
86,0
Kalan -
0,02
-
0,05
-
0,3
-
0,05
-
0,1
- 8,8
CuZn20 CW503L min.
max.
79,0
81,0
Kalan -
0,02
-
0,05
-
0,3
-
0,05
-
0,1
- 8,7
CuZn30 CW505L min.
max.
69,0
71,0
Kalan -
0,02
-
0,05
-
0,3
-
0,05
-
0,1
- 8,5
CuZn37 CW508L min.
max.
62,0
64,0
Kalan -
0,05
-
0,1
-
0,3
-
0,1
-
0,1
- 8,4
CuNi12Zn24 CW403J min.
max.
63,0
66,0
Kalan -- -
0,3
11,0
13,0
-
0,03
-
0,03
-
0,5
8,7

Chemical Composition

Copper Alloy
UNS No.
Composition, %
Copper Lead (max.) Iron (max.) Zinc
C23000 84,0 - 86,0 0,05 0,05 Remainder
C24000 78,5 - 81,5 0,05 0,05 Remainder
C26000 68,5 - 71,5 0,07 0,05 Remainder
C27400 61,0 - 64,0 0,1 0,05 Remainder
Copper Alloy
UNS No.
Composition, %
Copper Nickel Lead max. Iron max. Manganese max. Zinc
C75700 63,5-66,5 11,0-13,0 0,05 0,25 0,50 Remainder

Mechanical Properties

Production Range and Packaging Options